    • Non-linear optical properties of transparent glass-ceramics based on Co2+:Zn(Al,Ga)2O4 spinel nanocrystals 

      Glazunov, I.; Malyarevich, A.; Yumashev, K.; Dymshits, O.; Alekseeva, I.; Zhilin, A. (БНТУ, 2021)
      Transparent glass-ceramics containing Co2+:Zn(Al,Ga)2O4 spinel nanocrystals with sizes of 6–11 nm were studied. Absorption band of the Co2+ ions in the material is shifted to longer wavelengths as compared with glass-ceramics with no Ga2O3 addition. Absorption saturation at 1.54 μm was observed. The developed glassceramics is promising as saturable absorbers for 1.6 μm erbium lasers.
      2022-02-02

    • Novel NIR-to-NIR up-conversion phosphor for enhancing solar cell efficiency 

      Vilejshikova, E.; Khomenko, E.; Loiko, P.; Dymshits, O. (БНТУ, 2016)
      Novel NIR-to-NIR up-conversion phosphor for enhancing solar cell efficiency / E. Vilejshikova [et al.] // Сборник материалов 72-й студенческой научно-технической конференции, 20-28 апреля 2016 г. / Белорусский национальный технический университет, Факультет горного дела и инженерной экологии. Секция Английский язык. - Минск, 2016. – С. 312-315.
      2017-02-03

    • Optical properties of spinel based glass-ceramics of the Zno-Al2O3-Ga2O3-SiO2 system doped with Co2+ ions 

      Malyarevich, A.; Yumashev, K.; Dymshits, O.; Alekseeva, I.; Zhilin, A. (БНТУ, 2022)
      Transparent glass-ceramics containing Co2+:Zn(Al,Ga)2O4 spinel nanocrystals with sizes of 6–11 nm were studied. Absorption band of the Co2+ ions in the material is shifted to longer wavelengths as compared with glass-ceramics with no Ga2O3 addition. Absorption saturation at 1.54 μm was observed and its characteristics (absorption recovery time, ground-state and excited-state ...
      2022-12-28